Stainless Steel Composite Panel
Stainless Steel Composite Panel
  • Description
  • TECHNOLOGY PARAMETER
ALUBANG stainless steel composite panel has extraordinary ability in flatness and rigidity and high peel strength. The high strength advantage enables the panel a perfect material for the modern designs. In the past, this technology is monopolized by some steel mill only. After long time effort, our R&D team achieve success. With more than one decade experience in composite panel manufacturing field, we provide various specification for your reference.
ALUBANG stainless-steel composite panel is with top and back skin 0.3-0.4mm thick stainless-steel sheets, laminating to a mineral FR core or LDPE core in middle, overall thickness 4-6mm. The adhesion of metal and mineral is under help of macromolecule film at nanometer level, in addition to the help of ALUBANG high-tech continuous lamination line, the composite structure turns out to be integrated and solid.

Raw Material
Top Skin: 304 Stainless steel
Core Material: Non-toxic low-density polyethylene or Fire-resist
Bottom Skin: 304 stainless steel

Characteristics of Stainless Steel Composite Panel
1.Attains great mechanical quality while reduce the cost greatly, 4mm composite stainless-steel composite panel compete to 3mm solid stainless steel in this sense while the cost only half of it.
2.Stainless steel composite panel also attains Anti-crash quality with the help of mineral core layer especially during fabricating, installing or transporting. The best feature is its application in buildings, the surface effect is much soft and beauty.
3.Light weight with superior flatness

Mechanical Property

No.

Test Item

Test method

result

1

Density

ASTM D792-08 Method B

2.493g/cm3

2

Tensile strength

ASTM D638-10

105MPa

3

Flexural strength

ASTM D790-10 Procedure A

174MPa

4

Flexural modulus

ASTM D790-10 Procedure A

9670MPa

5

Shear strength

ASTM D732-10

96.4MPa

6

Shear resistance

ASTM D732-10

32248N

7

180°Peel strength

ASTM D903-98

1.18kgf/mm

8

Peel torque

ASTM D1781-98

34.2mm.kgf/mm

9

Heat deflection temperature

ASTM D648-07 Method B

91.1 ℃

10

Coefficient of linear thermal expansion

ASTM D969-08

227.5*10-6

*Test is based on 0.4mm #304 skin 4mm composite panel.


Standard (mm)

More Choice (mm)

Panel Thickness

4

3, 5, 6

Stainless-steel Alloy

#304

#316, #220

Stainless-steel Thickness

0.3

0.2, 0.4

Panel Width

1200

980, 1000, 1500

Panel Length

2440, 3200

1000~4000

Product Catalog